Synthesis of novel molecular sieves using a metal complex as a template

ABSTRACT

The synthesis and characterization of novel molecular sieves containing bis(pentamethylcyclopentadienyl) cobalt(III) ion are described. Several types of molecular sieves were prepared using the cobalt metal complex as a template that was shown to be incorporated as a guest molecule within the molecular sieve. Molecular sieves prepared using bis(pentamethylcyclopentadienyl) cobalt(III) ion as template were characterized as having a pore size at least as large as 7 Å. Other molecular sieves were also prepared using bis(cyclopentadienyl) cobalt(III) templates. The compounds are attractive as catalysts in a wide range of applications.

The United States Government has rights in the present invention pursuant to grant CHE-9157014 awarded by the National Science Foundation.

This is a divisional of application Ser. No. 08/296,488 filed Aug. 24, 1994, now U.S. Pat. No. 5,489,424.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The invention relates generally to synthesis of molecular sieve complexes and more specifically to the use of certain bis(cyclopentadienyl) cobalt ion complexes as structure directing agents or templates.

2. Description of Related Art

The incorporation of metal complexes during the synthesis of molecular sieves is known to be useful for synthesis of zeolite "Ship-in-a-bottle" complexes. NaX zeolites have been synthesized around metal phthalocyanines (Balkus, et al, 1992; Balkus and Kowalak, 1992). In a few cases the metal complex may also function as a structure directing agent during crystallization. The metal complex bis(cyclopentadienyl)cobalt(III) ion, Cp₂ Co⁺, has been reported to be a template for isostructural ZSM-51 and Nonasil in hydroxide and fluoride media as well as ZSM-45 (Balkus and Shepelev, 1993A, 1993B; U.S. Pat. No. 4,568,654). Nonasil is described in U.S. Pat. No. 4,556,549 as an all-silica clathrasil type molecular sieve. The metal complex is completely encapsulated as indicated by the x-ray structure that shows the largest openings to the nonasil cages are 6-membered rings (Behrens and van de Goor, 1994).

The formation of many molecular sieves depends on the presence of template molecules that affect the gel chemistry and/or act as a void filler (R. Szostak, 1989). Most of the templates that have been evaluated for molecular sieve synthesis are based on organic molecules, particularly aliphatic amines. By comparison, the structure directing properties of metal complexes are relatively unexplored. Cobalticinium ion, Cp₂ CO⁺, has been shown to be a template for the clathrate type molecular sieves Nonasil and ZSM-51 as well as ZSM-45. In the case of ZSM-51, the template claimed for its synthesis was bis(cyclopentadienyl) cobalt(III) hexafluorophosphate. More recently, Cp₂ CoOH was shown to be a template for the aluminum phosphate molecular sieves AlPO₄ -5 and AlPO₄ -16. Cp₂ Co⁺ has been reported to produce the all-silica clathrasils octadecasil and dodecasil.

Recent work has thus indicated that the role of the metal and the effect of functionalizing the bis(cyclopentadienyl) rings may lead to new types of molecular sieves when these agents are used as structure directing agents. However, the structure directing effects for synthesis of molecular sieves are largely unpredictable and not well understood. The availability of novel molecular sieves would be beneficial in extending the range of zeolite type catalysts and in semiconductor applications.

SUMMARY OF THE INVENTION

The present invention addresses problems inherent in the art by providing novel molecular sieve compounds and processes for producing the novel compounds. The present work shows that certain metal complexes can be employed as templates or structure-directing agents. Several new molecular sieve compounds have been produced. The compounds are microcrystalline and microporous and incorporate the templating agent metal used in the formation of the compound.

In particular, bis(cyclopentadienyl)cobalt(III) ion (Cp₂ Co⁺), has been shown to be a template for synthesis of the aluminum phosphate molecular sieves exemplified by AlPO₄ -5 and AlPO₄ -16. This is an unexpected finding to the extent that this metal complex will provide a template for both channel (AlPO₄ -5) and cage (AlPO₄ -16) molecular sieves. The Cp₂ Co⁺ complex is relatively rigid, unlike many typical organic templates. This provides an opportunity to evaluate the effects of size, shape and symmetry on the structure directing properties of the complex by the modifying the Cp ring(s) with different substituents.

Employing a fully methylated derivative, bis(pentamethylcyclopentadienyl) cobalt(III) ion (Cp₂ ^(*) Co⁺), the inventor has produced five new molecular sieves. It is contemplated that other new molecular sieves can be produced by altering the template; for example, any combination of alkyl groups on the cyclopentane ring such as methyl, ethyl, propyl, etc. as well as various metal species such as Ni²⁺, Fe²⁺, and other Group VIII metal ions. Nevertheless, the properties of these templates would be expected to differ from the bis pentamethylcyclopentadienyl species employed in the present invention.

The different metal complexes so far studied have unique structure directing properties, such that bis(cyclopentadienyl)cobalt(III) ion does not promote formation of the same structures as bis(pentamethylcyclopentadienyl) cobalt(III) ion. This is likely due to the different features of each complex, including size, shape and charge distribution.

Overall, and in general, the invention discloses novel microcrystalline molecular sieves prepared from template directing metallo organic complexes. In particular embodiments, a metal microcrystalline silica molecular sieve with a nominal pore diameter of at least 7.2 Å is formed. Such silica molecular sieves incorporate the positively charged metal ion as a guest molecule. Among the unique structures produced using the (Cp₂ ^(*) Co⁺) ion is a microcrystalline silica molecular sieve characterized as a yellow crystalline product, UTD-1. UTD-1 was prepared as a single phase product employing bis(pentamethylcyclopentadienyl) cobalt(III) ion as template. The crystalline material was formed from a gel containing sodium hydroxide, the organic metal template and fumed silica. UTD-1 is formed from a gel with the approximate molecular ratio of water to SiO₂ of about 60, sodium ion to SiO₂ of about 0.1, hydroxyl ion to silica SiO₂ of about 0.2 and the bis(pentamethylcyclopentadienyl) cobalt(III) ion template ratio to SiO₂ of about 0.1. The x-ray diffraction powder patterns for the UTD-1 as synthesized and the calcined material indicate the uniqueness of the molecular sieve. As expected, there is decomposition of the organic portion of the template after calcination at 500° C. The overall structure, however, is quite stable. The bright yellow color of UTD-1 indicates that the pentacyclodienyl metal ion complex is entrapped in the crystals as a guest molecule. The metal complex template is relatively large and is not removed by either aqueous or organic extraction procedures. Channels or cages within the molecular complex therefore are at least as large as the Cp^(*) rings that measure approximately 7.2 Å. UTD-1 is also a relatively large pore material as suggested by the low angle reflections obtained on x-ray crystallographic measurement.

While UTD-1 is quite stable, there is an indication of decomposition at approximately 350° C. Calcination is accompanied by a change in color from yellow to pale green. It is likely that this change of color represents decomposition of the organic portion of the metal complex with concomitant formation of metal oxide. There was no evidence of framework substitution by the cobalt during formation of the molecular sieve.

Yet another embodiment of the present invention is illustrated in the formation of the molecular sieve UTD-2. This compound also incorporates Cp^(*) ₂ Co as a guest molecule but is different in structure in incorporating aluminum and phosphorous as part of the framework. UTD-2 is also obtained as a single phase product from a gel having molar ratios of 1:0.9:0.4:0.86:0.025:50 for the components Al₂ O₃ :P₂ O₅ :SiO₂ :(TPA)₂ O:(CP^(*) ₂ Co)₂ O:H₂ O. Of course, these ratios may be varied somewhat. The preferred Al₂ O₃ /SiO₂ molar ratio is 2.5, although ranges as high as 4 or as low as 1 are also suitable. Using ratios outside of the range 4>2.5>1 typically results in an amorphous material. A convenient procedure for the preparation of UTD-2 and similar molecular sieves is to prepare two mixtures; mixture 1 from aluminum hydroxide and phosphoric acid and mixture 2 from silica, preferably fumed silica, CP^(*) ₂ Co⁺ hydroxide, and tetrapropylammonium hydroxide. Of course, one may vary not only the ratios but the type of quaternary ammonium compound employed; for example, other tetra alkyl ammonium hydroxides. UTD-2 is conveniently formed after mixing mixture 1 and mixture 2, heating for a period of time at approximately 200° C. cooling, diluting and separating the crystalline material. UTD-2, like UTD-1, is yellow, indicating inclusion of the metal template within the molecular sieve.

The novel compound UTD-2 may also be prepared using only Cp^(*) ₂ CoOH as template. The presence of tetrapropyl ammonium hydroxide, however, appears to be conducive to obtaining better yields of UTD-2. When using only Cp^(*) ₂ CoOH as the template, gels with molar ratios of about 1:0.9:0.4:0.32:50 to Al₂ O₃ :P₂ O₅ :SiO₂ (Cp^(*) ₂ Co)₂ O:H₂ O may be employed as preferred ratios. Variations of Al₃ /SiO₂ may be employed as previously discussed, preferably in the range of 4>2.5>1.

A new component, UTD-5, also resulted from the single template synthetic procedure used to obtain UTD-2. The new material UTD-5 was distinguishable from UTD-2 in its x-ray pattern as synthesized from the gel mixture and also after calcination at 500° C. The unusual dark green color of the calcined UTD-5 suggested formation of cobalt oxide and/or possibly the free metal.

Yet another embodiment of the present invention, the unsubstituted form of bis(cyclopentadienyl) cobalt(III), was used as a template to form a UTD-3/SAPO compound. The cobalt ion template was used in combination with tetrapropylammonium hydroxide. This compound was prepared using procedures analogous to those used to prepare UTD-2 except that the second mixture incorporated Cp₂ CoOH rather than Cp^(*) ₂ CoOH. Preferred molar ratios for Al₂ O₃ :P₂ O₅ :SiO₂ :(TPA)₂ O:(CP₂ CO)₂ O:H₂ O were about 1:0.9:0.4:0.86:0.025:48. The new UTD-3 SAPO compound was yellow in color, microcrystalline, and like the other compounds, changed color after calcination at 500° C. The new compound had a unique x-ray powder diffraction pattern. The calcined sample was a sky-blue color after heating for several hours at 500° C. UTD-3 could also be prepared as a single phase from the gel containing cobalt(II) ions instead of silica and Cp₂ CoOH as the only template. This UTD-3 compound is a modification of the UTD-3 to the extent that it is isolated as a dark blue-green product; however, it is single phase and has an x-ray diffraction pattern substantially the same as UTD-3. UTD-3-CoAPO is prepared by mixing phosphoric acid, a cobalt salt, preferably cobalt sulfate, then adding aluminum hydroxide and the bis(cyclopentadienyl) cobalt(III) hydroxide template, mixing the gel for several hours, e.g., approximately four hours, and then heating at about 200° C. for about a day, i.e., 18 to 24 hours, to provide a single phase product. Preferred molar ratios for Al₂ O₃ :P₂ O₅ :CoO:(Cp2Co)₂ O:H₂ O are about 0.8:1:0.4:0.75:53. However, the ratios may be employed within this general range to obtain UTD-3 CoAPO.

Yet another embodiment of the present invention UTD-6 may be prepared again employing the bis(pentamethylcyclopentadienyl) cobalt(III) template. In a particular embodiment, UTD-6 was prepared using two templates, the bis(cyclopentadienyl) complex and tetrabutylammonium hydroxide. The compound was prepared from a silicoaluminum phosphate gel. The preferred component molar ratios were about 1:0.9:0.4:0.86:0.16:75 for Al₂ O₃ :P₂ O₅ :SiO₂ :(TBA)₂ O:H₂ O. UTD-6 was conveniently prepared by admixing two mixtures; the first containing aluminum hydroxide and phosphoric acid; and the second containing fumed silica and the two templates.

The five new molecular sieve compounds described above are illustrative of the types of new compounds that may be prepared using a metal organic complex. For the first time, the inventors have shown the structure directing properties of cobalticinium ion complexes and that have demonstrated molecular sieves can be formed without an organo cation. The present invention illustrates the general types of novel structures that may be produced in the presence of bis(pentamethylcyclopentadienyl) cobalt(III) ion as the template. It is possible that even larger pore materials may be produced by increasing the bulkiness of the Complex cobalt(III) ion; for example, by appropriate substituent groups on the cyclopentane rings.

While the complete range of reactions and properties of the new microcrystalline metal molecular sieves has not been explored, it is recognized that related compounds have been well utilized as catalysts. More specifically, such compounds have been used in catalytic hydrofining, cracking, and as selective adsorbants. Many of these uses are described in more detail in U.S. Pat. No. 4,440,871 incorporated herein by reference where it is noted that in general silicon aluminum phosphate molecular sieves are similar to zeolite catalysts in several of their properties.

By analogy with the Cp₂ Co⁺ /nonasil complexes, the new molecular sieves are expected to exhibit special optical effects that could be exploited in memory storage devices. Molecular sieves are increasingly being developed as sensors in semiconductor devices.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1A. Powder x-ray diffraction pattern of UTD-1 as synthesized.

FIG. 1B. Powder x-ray diffraction pattern of UTD-1 after calcination (500° C., 4 hr) samples. CaF₂ was used as an internal standard.

FIG. 2. Scanning electron micrograph of UTD-1.

FIG. 3A. FT-IR spectra for UTD-1 as synthesized. Sample prepared as KBr pellet.

FIG. 3B. FT-IR spectrum of UTD-1 after calcination (500° C.) Sample prepared as KBr pellet.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The templating ability of metallocenes in the synthesis of crystalline microporous metal oxides is the general focus of the present invention. The inventors have prepared and characterized a series of novel silica type molecular sieves, designated as "UTD" compounds. The novel structures are produced in the presence of bis(pentamethylcyclopentadienyl)cobalt(III) ion, Cp^(*) ₂ Co⁺, as the template. Since the less bulky Cp₂ Co⁺ appeared to favor formation of the smaller pore clathrate type molecular sieves, the inventors have reasoned that addition of methyl groups to the cyclopentadienyl rings will encourage the crystallization of larger pore materials.

It is known that the crystallization of zeolite molecular sieves in the presence of metal chelates may result in encapsulation of the complexes (U.S. Pat. No. 5,167,942). This is a viable method for the preparation of zeolite ship-in-a-bottle complexes (Balkus and Gabrielov, 1994); however, the metal complex may also serve as a structure directing agent. The formation of many molecular sieves depends on the presence of template molecules that affect the gel chemistry and/or act as a void filler.

Most of the templates that have been evaluated for molecular sieve synthesis are based on organic molecules, especially aliphatic amines. By comparison, the structure directing properties of metal complexes are virtually unknown. Cobalticinium ion, Cp₂ Co⁺, has been shown to be a template for the clathrate type molecular sieves Nonasil and ZSM-51 (Balkus and Shepelev, 1993; Balkus and Shepelev, 1993B; U.S. Pat. No. 4,568,564). More recently, work in the inventors' laboratory showed that Cp₂ CoOH acts as a template for the production of AlPO₄ -16 and SAPO-16. Molecular sieves of this type had previously required an organo-cation to form and, specifically in the case of AlPO₄ -16 or SAPO-16, only quinuclidene was known to generate this topology.

The following examples are provided for purposes of clarification and should not be considered as limiting. One skilled in the art would recognize in light of the present disclosure that although the specified materials and conditions are important in practicing the invention, unspecified materials and conditions are not excluded as long as they do not prevent the benefits of the invention from being realized.

EXAMPLE 1

This example illustrates the preparation of an all-silica molecular sieve using a bis(pentamethylcyclopentadienyl) cobalt(III) ion as a template. The microcrystalline silica molecular sieve incorporates the complexed cobalt ion, apparently as a guest molecule.

Preparation of UTD-1

The metal complex Cp^(*) ₂ CoPF₆ was prepared according to the literature procedure (Kolle and Khouzami, 1981). The complex was converted to the chloride derivative over Dowex-50W cation exchange resin by first adsorbing the Cp^(*) ₂ Co⁺ ion followed by elution with 1M HCl. The Cp^(*) ₂ CoCl was then transformed to the hydroxide form over an aqueous slurry of silver oxide at 70° C. The concentration of the brown Cp^(*) ₂ CoOH solution was determined by potentiometric titration. The solution was then used in the molecular sieve synthesis.

UTD-1 was prepared as a single phase product by combining NaOH, a 31.6% aqueous Cp^(*) ₂ CoOH solution and fumed silica to form a gel with the following molar ratios.

    ______________________________________                                                 H.sub.2 O/SiO.sub.2                                                                     60                                                                    Na.sup.+ /SiO.sub.2                                                                     0.1                                                                   OH.sup.- /SiO.sub.2                                                                     0.2                                                                   CP*.sub.2 Co.sup.+ /SiO.sub.2                                                           0.1                                                           ______________________________________                                    

The gel was aged with stirring for 1 hour and then transferred to a 23 mL Teflon-lined pressure reactor (Parr). The reactor was heated at 175° C. under static conditions for 2 days. The resulting yellow crystalline product was washed with deionized water, suction filtered and then dried at 90° C. for 2 hours.

FIG. 1A shows the X-ray diffraction (XRD) powder pattern data for UTD-1 as synthesized. FIG. 1B shows the XRD of calcined UTD-1. Although there are changes in peak intensity after calcination at 500° C. and decomposition of the template occurs, the structure appears quite stable. FIG. 2 shows the bundles of rectangular shaped crystals obtained after synthesis. These results support a single phase material. The bright yellow color of UTD-1 indicated that the Cp^(*) ₂ Co⁺ template was entrapped in the crystals as a guest molecule. The metal complex cannot be removed by aqueous or organic extraction. This implied that the channels or cages were at least as large as the Cp^(*) rings (7.2 Å) in order to accommodate the complexes. The low angle reflections in FIGS. 1A and 1B also suggested a large pore material. Additionally, preliminary adsorption experiments using calcined UTD-1 indicated a ˜20% by weight increase upon exposure to cyclohexane (kinetic diameter 6.0 Å). Pore size determination by more direct adsorption methods is complicated by the occluded cobalt species.

                  TABLE 1A                                                         ______________________________________                                         (UTD-1 as synthesized)                                                                      d     %                                                           ______________________________________                                         1.             14.686  48                                                      2.             11.742  44                                                      3.             8.068   6                                                       4.             7.339   23                                                      5.             6.058   53                                                      6.             5.872   8                                                       7.             6.459   50                                                      8.             4.9754  50                                                      9.             4.892   10                                                      10.            4.553   100                                                     11.            4.031   57                                                      12.            4.193   25                                                      13.            3.913   15                                                      14.            3.829   5                                                       15.            3.710   5                                                       16.            3.668   41                                                      17.            3.611   34                                                      18.            3.448   4                                                       19.            3.390   23                                                      20.            3.206   5                                                       21.            3.084   11                                                      22.            3.006   23                                                      23.            2.799   8                                                       24.            2.763   18                                                      25.            2.738   3                                                       26.            2.637   4                                                       27.            2.509   4                                                       28.            2.489   3                                                       29.            2.445   7                                                       30.            2.406   3                                                       ______________________________________                                    

                  TABLE 1B                                                         ______________________________________                                         (calcined at 500° C.)                                                           d     %                                                                ______________________________________                                                 14.620                                                                               100                                                                      11.509                                                                               64                                                                       9.466 6                                                                        6.094 10                                                                       4.882 13                                                                       4.478 23                                                                       4.384 7                                                                        4.211 45                                                                       4.049 10                                                                       3.955 6                                                                        3.843 5                                                                        3.735 2                                                                        3.659 17                                                                       3.560 14                                                                       3.400 9                                                                        3.066 3                                                                        3.066 5                                                                        2.769 6                                                                        2.646 1                                                                        2.553 1                                                                        2.466 1                                                                        2.436 2                                                                        2.374 2                                                                ______________________________________                                    

There was no evidence of complex decomposition during synthesis from spectroscopic analysis of encapsulated and free complexes. The UV-Vis spectrum of a UTD-1 nujol mull was broadened and slightly red shifted (<15 nm) compared to an aqueous solution of Cp^(*) ₂ CoOH (290, 338sh, 406sh nm). However, this shift to lower energy was also noted for Cp₂ Co⁺ in Nonasil and AlPO₄₋ 5 molecular sieves (Balkus and Shepelev, 1993A). Thermogravimetric analysis (TG) of Cp^(*) ₂ CoPF₆ indicated the onset of decomposition at ˜350° C., which is significantly higher than the UTD-1 synthesis temperature (175° C.). Similarly, UTD-1 begins to lose weight at ˜350° C. with a change in color from yellow to pale green. Only a 5% weight change was measured up to 900° C. The small change is consistent with loss of the organics and probable formation of occluded oxides.

There was no evidence of framework substitution by cobalt. The FT-IR spectrum of UTD-1 also indicated the presence of intact Cp^(*) ₂ Co⁺ as evidenced by the ν_(CH) at 2915 cm⁻¹ that can be compared to the free Cp^(*) ₂ CoPF₆ complex with a C--H band at 2920 cm⁻¹. Similarly, a C--C stretch at 1476 cm⁻¹ for the free complex appeared at 1480 cm⁻¹ in UTD-1. There were a variety of other bands that might be ascribed to the encapsulated metal complex; however, they were either masked by the bands associated with the molecular sieve or were quite weak.

FIG. 3A shows the FT-IR spectrum in the region 1500-400 cm⁻¹ for UTD-1 as synthesized. FIG. 3B shows the FT-IR spectrum after calcination at 500° C. There are two strong bands at 1237 and 1092 cm⁻¹ that are typical of the asymmetric Si--O stretches observed for crystalline silicates. There are no significant shifts for these bands after calcination; however, two shoulders are resolved at 1140 and 1076 cm⁻¹. The bands that appear in the symmetric stretching region (812, 787, 642 cm⁻¹), as well as the more structure sensitive region (612, 582 and 537 cm⁻¹), appear quite different from known silicate phases.

The results indicate that an all-silica phase UTD-1 can be synthesized using the metal complex Cp^(*) ₂ CoOH as a template that becomes incorporated as a guest molecule. The data indicate that UTD-1 is a large pore material (>7 Å).

EXAMPLE 2

Another new molecular sieve was prepared as illustrated in the following example. This compound, like UTD-1, also incorporates the template Cp^(*) ₂ Co⁺ as a guest molecule but differs in including aluminum and phosphorus as part of the framework.

Preparation of UTD-2

UTD-2 was obtained as a single phase product from a gel having molar ratios Al₂ O₃ :P₂ O₅ :SiO₂ :(TPA)₂ O:(CP^(*) ₂ Co)₂ O:H₂ O--1:0.9:0.4:0.86:0,025:50. The preferred Al₂ O₃ /SiO₂ molar ratio is 2.5. Taking the Al₂ O₃ /SiO₂ ratios out of the range 4>2.5>1 may result in an amorphous material. The procedure involves first preparing two mixtures as follows.

Mixture 1 was prepared by slowly adding 2 g of aluminum hydroxide (Pfaltz & Bauer, LOT 039789, 83.34 wt %) to a solution of 2.22 g 85 wt % H₃ PO₄ (Fisher) and 2.0 g of deionized water with magnetic stirring. After adding about 1.3 g of the hydroxide, the gel became extremely viscous and was stirred with a Teflon rod for 1 hour.

Mixture 2 was prepared by adding 0.256 g fumed silica (0.007 μ, Aldrich) to a mixture of 0.58 g of a 30 wt % Cp^(*) ₂ CoOH solution in water and 9.28 g of 40 wt % tetrapropylammonium hydroxide (TPAOH obtained from Alfa). Mixture 2 was not viscous and easily obtained homogeneity.

Mixture 2 was added slowly to mixture 1 and the final mixture was stirred for approximately 6 hours in order to achieve a homogeneous gel. The gel was transferred into a 25 cm³ Teflon-lined pressure reactor (Parr) that was subsequently placed in an oven having a constant temperature of 200° C. After 20 hrs heating at autogenous pressure, the mixture was cooled to room temperature and diluted with 100 mL of deionized water. The bright yellow crystals were separated from a white amorphous material by centrifugation and/or sedimentation, washed with deionized water and isolated by filtering through a nitrocellulose membrane (2 μm) under suction. The solid yellow residue was dried at room temperature for 24 hrs. UTD-2 appeared on SEM images as a single phase.

                  TABLE 2                                                          ______________________________________                                         X-ray pattern for UTD-2 as synthesized                                         #      2 theta       d, A    (rel.int., %)                                     ______________________________________                                         1.     6.270         14.085  (100)                                             2.     11.307        7.819   (4)                                               3.     11.720        7.545   (3)                                               4.     12.542        7.052   (9)                                               5.     18.844        4.705   (27)                                              6.     19.272        4.602   (50)                                              7.     20.267        4.378   (23)                                              8.     23.014        3.861   (2)                                               9.     25.215        3.529   (61)                                              10.    27.062        3.292   (6)                                               11.    31.903        2.803   (3)                                               12.    33.695        2.658   (12)                                              13.    34.283        2.614   (7)                                               14.    36.014        2.492   (1)                                               15.    38.165        2.356   (1)                                               ______________________________________                                    

EXAMPLE 3

UTD-2 could be also obtained using only Cp^(*) ₂ CoOH as template, as shown in the following example.

Single Template Synthesis of UTD-2

The single template synthesis of UTD-2 was substantially the same as that described in Example 2 except that mixture 2 was prepared by adding 0.256 g fumed silica to 7.76 g of a 30 wt % Cp^(*) ₂ CoOH solution in water. The final gel had molar ratios Al₂ O₃ :P₂ O₅ : SiO₂ :(Cp^(*) ₂ Co)₂ O:H₂ O=1:0.9:0.4:0.32:50. The x-ray pattern of the yellow sample obtained after crystallization and purification indicated the presence of UTD-2 (about 30%) and a second component, UTD-5. Most of the peaks of UTD-5 are broad. UTD-5 was isolated by sedimentation and/or centrifugation of the more dense layer.

                  TABLE 3                                                          ______________________________________                                         X-ray Pattern for UTD-5 as Synthesized                                         #      2 theta       d, A   (rel.int., %)                                      ______________________________________                                         1      6.51          13.57  (24)                                               2      10.89         8.12   (16)                                               3      12.31         7.18   (21)                                               4      12.92         6.85   (31)                                               5      13.12         6.740  (30)                                               6      16.78         5.28   (55)                                               7      20.88         4.25   (100)                                              8      22.12         4.02   (71)                                               9      23.13         3.84   (25)                                               10     26.51         3.36   (24)                                               11     29.21         3.06   (31)                                               12     32.07         2.79   (20)                                               ______________________________________                                    

                  TABLE 4                                                          ______________________________________                                         X-ray pattern for UTD-5 calcined at 500° C. (dark green)                #      2 theta       d, A   (rel.int., %)                                      ______________________________________                                         1      6.48          13.63  (92)                                               2      7.52          11.75  (46)                                               3      12.45         7.10   (42)                                               4      21.04         4.22   (96)                                               5      21.30         4.17   (100)                                              6      22.30         3.98   (62)                                               7      24.48         3.63   (33)                                               ______________________________________                                    

EXAMPLE 4

This example illustrates the formation of a novel microcrystalline molecule sieve using bis(cyclopentadienyl) cobalt(III) ion as the template.

Preparation of UTD-3-SAPO

Mixture 1 was prepared as described in Example 2. Bis(cyclopentadienyl)cobalt(III) hydroxide (Cp₂ CoOH) was used as a template in combination with tetrapropylammonium hydroxide (TPAOH).

Mixture 2 was prepared by adding 0.256 g fumed silica to a mixture of 0.354 g of a 31 wt % Cp₂ CoOH solution in water and 9.28 g of 40 wt % tetrapropylammoniumhydroxide. The molar ratios were as follows: Al₂ O₃ :P₂ O₅ :SiO₂ :(TPA)₂ O:(Cp₂ Co)₂ O:H₂ O=1:0.9:0.4:0.86: 0.025:48. The crystallization and purification procedures were similar to those described in Example 2. The top and bottom layers (white material) were separated from the intermediate bright yellow fraction by sedimentation and/or centrifugation. The yellow fraction was isolated as UTD-3. The yellow sample turned sky-blue after calcination at 500° C. X-ray powder diffraction patterns for UTD-3 are shown in Table 5 for the synthesized compound and in Table 6 after calcination.

                  TABLE 5                                                          ______________________________________                                         X-ray pattern for UTD-3 as synthesized (yellow)                                #      2 theta       d, A    (rel.int., %)                                     ______________________________________                                         1      8.588         10.288   (3)                                              2      10.898        8.112    (5)                                              3      15.936        5.557   (11)                                              4      17.279        5.128   (80)                                              5      17.694        5.009   (14)                                              6      20.805        4.266   (23)                                              7      21.919        4.052   (100)                                             8      23.278        3.818   (37)                                              9      24.790        3.589    (4)                                              10     26.938        3.307    (6)                                              11     28.226        3.159   (20)                                              12     31.313        2.854    (4)                                              13     32.171        2.780   (24)                                              14     34.202        2.620   (14)                                              15     34.956        2.565    (8)                                              16     35.881        2.507    (5)                                              ______________________________________                                    

                  TABLE 6                                                          ______________________________________                                         X-ray pattern for UTD-3 calcined 550° C. (blue color)                   #      2 theta       d, A    (rel.int., %)                                     ______________________________________                                         1      8.639         10.227  (15)                                              2      10.926        8.091   (49)                                              3      13.466        6.570   (51)                                              4      15.903        5.568   (15)                                              5      17.292        5.124   (78)                                              6      17.642        5.023   (13)                                              7      20.832        4.261   (44)                                              8      21.946        4.074   (100)                                             9      23.279        3.818   (31)                                              10     24.885        3.575   (13)                                              11     26.991        3.301   (15)                                              12     28.226        3.159   (20)                                              13     29.316        3.044   (11)                                              14     32.229        2.775   (24)                                              15     32.375        2.763   (25)                                              16     34.264        2.615   (13)                                              17     37.714        2.383   (11)                                              ______________________________________                                    

EXAMPLE 5

UTD-3 can be prepared as a single phase from the gel containing Co²⁺ ions instead of silica and Cp₂ CoOH as the only template.

Synthesis of UTD-3-CoAPO

3.4 g H₂ O and 3.10 g 85% H₃ PO₄ were mixed with 1.5 g CoSO₄ 7H₂ O and stirred for thirty minutes. 2.0 g Al(OH)₃ (83.34%) was slowly added to the solution and mixed for 1 hr. Then, 13.4 g of a 26.6% Cp₂ CoOH solution was added to the mixture. The molar ratios were Al₂ O₃ :P₂ O₅ :CoO:(Cp₂ Co)₂ O:H₂ O=0.8:1:0.4:0.75:53. The gel was mixed for 4 hrs, and then placed in an oven at 200° C. for 19 hours. The dark blue-green product was a pure single phase. The x-ray pattern was similar to that of UTD-3 shown in Table 5.

EXAMPLE 6

The compound described in the following example was prepared using two templates, one of which was Cp^(*) ₂ CoOH.

Preparation of UTD-6

UTD-6 was prepared from silicoaluminum phosphate gel using a Cp^(*) ₂ CoOH and tetrabutylammonium hydroxide (TBAOH) as templates. The molar ratios were Al₂ O₃ :P₂ O₅ :SiO₂ :(TBA)₂ O:H₂ O=1:0.9:0.4:0.86:0.16:75.

Mixture 1 was prepared by slow addition of 2 g of aluminum hydroxide (Pfaltz & Bauer, LOT 039789, 83.34 wt %) to a solution of 2.22 g 85 wt % H₃ PO₄ (Fisher) and 2.0 g of deionized water with magnetic stirring. After addition of about 1.3 g of the hydroxide, the gel became extremely viscous and was stirred with a Teflon rod for 1 hour.

Mixture 2 was prepared by adding 0.256 g fumed silica (0.007 m, Aldrich) to a mixture of 4.34 g of a 26.6 wt % Cp^(*) ₂ CoOH solution in water and 11.92 g of 40 wt % TBAOH (obtained from Alfa). Mixture 2 was not viscous and easily obtained homogeneity.

Mixture 2 was added slowly to mixture 1 and the final mixture was stirred for approximately 6 hrs in order to achieve a homogeneous gel. The gel was transferred into a 25 cm³ Teflon-lined pressure reactor (Parr) that was subsequently placed in an oven having a constant temperature of 200° C. After 20 hours heating at autogeneous pressure, the mixture was cooled to room temperature and diluted with 100 mL of deionized water. The yellow product was isolated by filtration and washed with copious amounts of water.

                  TABLE 7                                                          ______________________________________                                         X-ray pattern for UTD-6 as synthesized                                         #      2 theta       d, A   (rel.int., %)                                      ______________________________________                                         1      5.35          16.49  (100)                                              2      6.44          13.72  (61)                                               3      11.90         7.43   (21)                                               4      17.49         5.07   (71)                                               5      19.77         4.49   (43)                                               6      29.03         3.07   (50)                                               7      30.91         2.89   (25)                                               8      35.30         2.54   (32)                                               9      35.74         2.51   (21)                                               10     35.81         2.50   (21)                                               ______________________________________                                    

REFERENCES

The following references to the extent that they provide exemplary procedural or other details supplementary to those set forth herein are specifically incorporated herein by reference.

K. J. Balkus, Jr. and S. Kowalak, U.S. Pat. No. 5,167,942, 1992.

K. J. Balkus, Jr. and S. Shepelev, Micropor. Mater., 1993A, 1, 383.

K. J. Balkus, Jr. and S. Shepelev, Petrol. Preprints, 1993B, 38, 512.

Behrens, P. and van de Goor, G.

E. W. Valyecsik, U.S. Pat. No. 4,568,654, 1986.

Valyecsik, E. W., U.S. Pat. No. 4,556,549 (Dec. 3, 1985).

U. Kolle and F. Khouzami, Chem. Ber., 1981, 114, 2929.

Balkus, K. J., Jr., Hargis, C. D. and Kowalak, S., ACS Symp. Ser. 449, 348 (1992).

Szostak, R. in Molecular Sieves, Van Nostrand, New York, N.Y., p. 79, 84, 1989. 

What is claimed is:
 1. A metal microcrystalline silicoaluminophosphate molecular sieve having a nominal pore diameter greater than about 7.2. A and comprising Al₂ O₃ and SiO₂ in a molar ratio of about 2.5 and (Cp^(*) ₂ Co)₂ O where Cp^(*) ₂ Co is bis(pentamethylcyclopentadienyl) cobalt III ion.
 2. The metal microcrystalline silicoaluminophosphate molecular sieve of claim 1 wherein said compound is prepared from a gel comprising Al₂ O₃, P₂ O₅, SiO₂, (TPA)₂ O, (Cp^(*) ₂ Co)₂ O and H₂ O in a molar ratio of about 1:0.9:0.4:0.86:0.025:50 where Cp^(*) ₂ Co is bis(pentamethylcyclopentadienyl) cobalt (III) ion and TPA is tetrapropylammonium ion.
 3. The metal microcrystalline silicoaluminophosphate molecular sieve of claim 1 which is identified as UTD-2.
 4. The metal microcrystalline silicoaluminophosphate molecular sieve of claim 1 that as synthesized has an x-ray diffraction pattern including lines shown in Table
 2. 5. The metal microcrystalline silicoaluminophosphate molecular sieve of claim 1 that is prepared from a gel comprising Al₂ O₃, P₂ O₅, SiO₂, (Cp₂ ^(*) Co)₂ O and H₂ O in a molar ratio of 1:0.9:0.4:0.32:50 where (Cp^(*) ₂ Co)₂ is bis(pentamethylcyclopentadienyl) cobalt (III) ion and wherein said molecular sieve has an x-ray diffraction pattern as synthesized including lines shown in Table
 3. 6. The metal microcrystalline silicoaluminophosphate molecular sieve of claim 5 wherein the molar ratio of Al₂ O₃ :P₂ O₅ :SiO₂ :(Cp^(*) ₂ Co)₂ O:H₂ O is 1:0.9:0.4:0.32:50 which is identified as UTD-5.
 7. A microcrystalline silicoaluminophosphate molecular sieve prepared from a gel comprising Al₂ O₃, P₂ O₅, SiO₂, (TPA)₂ O, (Cp₂ Co)O₂ and H₂ O in a molar ration of about 1:0.9:0.4:0.86:0.025:48 where Cp₂ CO is bis(cyclopentadienyl)cobalt(III) ion and TPA is tetrapropylammonium ion and wherein said molecular sieve as synthesized exhibits an x-ray diffraction pattern including lines shown in Table
 5. 8. A microcrystalline silicoaluminum phosphate molecular sieve that is prepared from a gel having a molar ratio of Al₂ O₃ :P₂ O₅ :CoO:(Cp₂ Co)₂ O:H₂ O equal to about 0.8:1:0.4:0.75:53 wherein (Cp₂ Co)₂ is bis(cyclopentadienyl) cobalt(III) ion that is included within the molecular sieve.
 9. A metal microcrystalline silica molecular sieve that has an x-ray powder diffraction pattern as synthesized including lines shown in Table
 3. 10. A metal microcrystalline silica molecular sieve that has an x-ray diffraction pattern after calcination that includes the lines set forth in Table
 4. 